Study of waterborne polyurethane materials under aging treatments. Effect of the soft segment length

Polyurethane (PU) films were obtained by water evaporation of the PU dispersions and they were annealed at 80 °C for 2 h. Accelerated aging studies were performed by submerging the PU films in the water at 80 °C for 2 h. The PU films synthesized with the polyols with lower molecular weight exhibited enhanced phase miscibility, giving place to storage and loss moduli of similar magnitudes in a wide temperature range and they were less susceptible to hydrolytic degradation. Microphase miscibility was favored when shorter polyols are used. Contact angle measurement and cross-hatch adhesion test on PU coatings placed on stainless steel plate, before and after annealing and water aging were carried out. All PU coatings retained the adhesion to the substrate after aging, the PU coatings synthesized with shorter polyols exhibited enhanced adhesion.