• HAP nanostructures have been prepared by a simple precipitation method.
• To control shape and particle size of HAP, different Schiff bases were employed.
• 0-D and 1-D HAP nanostructures have been formed by this method.
In this work, hydroxyapatite (HAP), Ca10(PO4)6(OH)2, nanostructures including nanorods, nanobundles and nanoparticles have been prepared via a simple precipitation method. In the present method, Ca(NO3)2·4H2O and (NH4)2HPO4 were used as calcium and phosphorus precursors, respectively. Besides, the Schiff bases derived from 2-hydroxyacetophenone and different diamines were used as complexing agents for the in situ formation of Ca2 + complexes. The formation mechanism of 0-D and 1-D nanostructures of HAP was also considered. When the complexing agents could coordinate to the Ca2 + ions through N and O atoms to form the [CaN2O2]2 + complexes, HAP nanoparticles were generated. On the other hand, nanorods and nanobundles of HAP were obtained by forming the [CaN2]2 + as well as [CaO2]2 + complexes in the reaction solution. This work is the first successful synthesis of pure HAP nanostructures in the presence of Schiff bases instead of using the common surfactants.
Figure optionsDownload as PowerPoint slide
Journal: Materials Science and Engineering: C - Volume 40, 1 July 2014, Pages 288–298