Enhanced properties of Al-modified EB-PVD 7YSZ thermal barrier coatings

7 wt% yttria-stabilized zirconia (7YSZ) thermal barrier coating (TBC) prepared by electron beam-physical vapor deposition (EB-PVD) has been used in gas turbine engines for many years, where the TBC must successfully withstands the damage caused by a variety of environmental and mechanical aspects. The primary failure modes for TBC are oxidation of bond coating, particle erosion and CMAS (calcium-magnesium-alumina-silicates) corrosion. The lifetime of TBC associated with above three failure factors will be reduced significantly. In order to prolong the operation time, an alternative approach depositing Al film on 7YSZ TBC surface by magnetron sputtering is proposed. An α-Al2O3 overlay was in-situ synthesized on each 7YSZ column through reaction of Al and ZrO2 during vacuum heat treatment. And the results indicate that the Al-modified EB-PVD 7YSZ TBC shows better oxidation resistance, as well as lower particulate erosion and CMAS corrosion.