![عکس صفحه اول مقاله: Preparation and mechanical performance of ductile Csf/Al2O3-BN composites, Part 1: Effects of fiber length and sintering temperature Preparation and mechanical performance of ductile Csf/Al2O3-BN composites, Part 1: Effects of fiber length and sintering temperature](/preview/png/1459061.png)
Since its invention, alumina ceramics have been extensively investigated for potential various applications. However, their intrinsic brittle nature is still an insurmountable obstacle when they are applied as structural components. This paper provides a simple routs to prepare ductile alumina based composites with the addition of chopped carbon fiber (Csf/Al2O3-BN). Effects of fiber length and sintering temperature on the microstructure, phase composition, mechanical properties together with fracture behavior were systematically investigated. The results showed that composites with mixed fiber lengths of 12 mm and 1 mm exhibited homogeneous microstructure and striking enhancement in mechanical performances compared with composites with other fiber length. With the increase in sintering temperature from 1500 °C to 1650 °C, interfacial bonding strength increased and interface state converted from mechanical interlocking at 1500 °C into chemical bonding at 1650 °C. Chemical reaction in the composites degraded carbon fiber properties, which resulted in the decrease in mechanical performance of the composites.
Journal: Ceramics International - Volume 42, Issue 8, June 2016, Pages 9821–9829