The accumulative damage behaviour of BN-coated Hi-Nicalon™ SiC fibre-reinforced SiC matrix composite was examined under tensile cyclic loading at room and elevated temperatures. The accumulative damage occurring during the cyclic loading was quantitatively characterised using the damage parameter obtained by the hysteresis loop curves. The damage parameter increased with increasing applied stress beyond the matrix cracking stress, and it subsequently retained a nearly constant value until just before fracture. Moreover, the dielectric constant, dielectric loss and loss tangent of the composite were measured before and after the fracture in the frequency range 1–1000 MHz. The dielectric properties had similar frequency dependency before and after the fracture. However, the dielectric constant, dielectric loss and loss tangent were lower in the post-fractured specimens than in the pristine ones. The reduction of the dielectric properties was associated with the accumulative damage stored in the specimens. In addition, the relationships between the dielectric properties and the damage parameter were described in detail.
Journal: Ceramics International - Volume 41, Issue 6, July 2015, Pages 7366–7373