Synthesis and luminescence properties of nitrided lanthanum magnesium hexaluminate LaMgAl11O19 phosphors
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Nitrided LaMgAl11O19 phosphors were prepared by a two-step method involving synthesis at 1550 °C for 4 h, trituration, and firing at 1650 °C for 5 h under a nitrogen atmosphere. Nitrogen was doped into LaMgAl11O19 and bonded with aluminium atoms. The nitrided LaMgAl11O19 phosphors showed plate-like morphology with a rough surface and exhibited strong blue emission at 442 nm and 450 nm, which may be attributed to the energy transition between defect levels. A weak emission band at 590 nm was ascribed to the transition between the VAl acceptor and the valence band, which was excited at 254 nm.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 40, Issue 3, April 2014, Pages 4535–4539
Journal: Ceramics International - Volume 40, Issue 3, April 2014, Pages 4535–4539
نویسندگان
Xin Min, Minghao Fang, Zhaohui Huang, Yan’gai Liu, Chao Tang, Tingting Qian, Xiaowen Wu,