The influence of laser treatment on thermal shock resistance of plasma-sprayed nanostructured yttria stabilized zirconia thermal barrier coatings

The main goal of this paper was to evaluate the effects of laser glazing on the microstructure and thermal shock resistance of nanostructured thermal barrier coatings (TBCs). To this end, nanostructured yttria stabilized zirconia (YSZ) top coat and NiCrAlY bond coat were deposited on Inconel 738LC substrate by air plasma spraying (APS). The Nd:YAG pulsed laser was used for laser treatment of top coat surface. The thermal shock behavior of plasma-sprayed and laser-glazed coatings was investigated by quenching the samples in cold water from 1000 °C. The microstructure and phase composition of the coatings were characterized by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). Energy dispersive spectroscopy (EDS) was used to analyze the interface diffusion behavior of the bond coat elements. The results of SEM revealed that the laser glazing process reduced the surface roughness, eliminated the porosity of the surface and produced network cracks perpendicular to the surface. XRD results also indicated that both as-sprayed and laser glazed coatings consisted of non-transformable (T′) phase. Thermal shock test results showed that the lifetimes of the plasma-sprayed TBCs were almost doubled by laser glazing. Continuous network of segmented cracks perpendicular to the surface produced by laser glazing improved the strain accommodation and recognized it as the main enhancement mechanism for TBC life extension.