Oxidation behavior of Si/SiC ceramic composite synthesized from processed cellulosic bio-precursor was studied in dry air over the temperature range 1200–1350 °C. The material was synthesized from processed bio-precursors (bleached bamboo kraft pulp in the form of flat board of bulk density 0.58 g cm−3) and had a bulk density of 2.66 g cm−3, porosity of 0.6 vol% and contents of Si and SiC phases of 39.1% and 60.3% (v/v) respectively. The process of oxidation could be described closely by a parabolic oxidation equation. An activation energy of 141.4 kJ/mol was obtained. Both the SiC and Si phases oxidized and the oxidation was mainly controlled by the transport of molecular oxygen through the growing oxide layer. Pre-oxidation at 1300 °C for 24 h in ambient air increased the strength of Si/SiC ceramics by around 46% because of the healing of the surface defects created during surface preparation by the oxide layer.
Journal: Ceramics International - Volume 38, Issue 6, August 2012, Pages 4701–4706