Microstructure and mechanical properties of the spark plasma sintered Ta2C ceramics
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
Microstructure and mechanical properties of the spark plasma sintered Ta2C ceramics
چکیده انگلیسی

Single phase hexagonal α-Ta2C ceramics were synthesized by spark plasma sintering and using TaC and Ta as the starting powders. Effects of sintering temperatures and holding times on the densification process, phase formation, microstructure development, and mechanical properties of the α-Ta2C ceramics were investigated. Densification occurred in the temperature range of 1520–1675 °C in less than 2.5 min. But completion of the Ta2C formation took about 40 min at 1500 °C, and 5 min at 1900 °C. The materials sintered at 1500 °C consisted of fine equiaxed grains. The Ta2C grains grew anisotropic to form an elongated self-toughening microstructure at 1700 °C. At 1900 °C, the neighboring Ta2C individual crystals coalesced to form large Ta2C blocks to entrap the residual pores. Although higher flexural strength and fracture toughness were reached at 1700 °C, the unstable microstructures of the Ta2C materials indicated limited applications at high temperatures.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 38, Issue 6, August 2012, Pages 4707–4713
نویسندگان
, , , , ,