Synthesis of NiWO4 nano-particles in low-temperature molten salt medium

Nickel tungstate (NiWO4) nano-particles were successfully synthesized at low temperatures by a molten salt method, and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and ultraviolet visible spectra techniques (UV–vis), respectively. The effects of calcining temperature and salt quantity on the crystallization and development of NiWO4 crystallites were studied. Experimental results showed that the well-crystallized NiWO4 nano-particles with about 30 nm in diameter could be prepared at 270 °C with 6:1 mass ratio of the salt to NiWO4 precursor. XRD analysis confirmed that the product was a pure monoclinic phase of NiWO4 with wolframite structure. UV–vis spectrum revealed that NiWO4 nano-particles had good light absorption properties in both ultraviolet and visible light region.