Wet-chemical synthesis of magnesium niobate nanoparticles powders
چکیده انگلیسی

Nanosized and highly reactive magnesium niobate (MgNb2O6MgNb2O6) powders were successfully synthesized by a new wet-chemical method by means of the dissolution of Nb2O5⋅5H2ONb2O5⋅5H2O and in a solution of oxalic acid followed by the addition of stoichiometric amounts of magnesium carbonate. The Nb–Mg–oxalic acid solution was evaporated resulting in a dry and amorphous powder that was calcined in the temperature range from 200 to 900 °C for 2 h. The crystallization process from the amorphous state to the crystalline MgNb2O6MgNb2O6 was followed by thermal analysis. The calcined powders characterized by FT-Raman spectroscopy, X-ray diffraction (XRD) and their morphology examined by high resolution scanning electron microscopy (HR-SEM). Pure MgNb2O6MgNb2O6, free from the second phases and obtained at 800 °C was confirmed by a combined analysis using XRD and FT-Raman. The average diameter of the particles was calculated from the HR-SEM image as 70 nm approximately. This technique allows a better mixing of the constituent elements and thus a better reactivity of the mixture to obtain pre-reaction products with high purity at lower temperatures and reducing cost. It can offer a great advantage in the PMN-PT formation with respect to the solid-state synthesis.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 33, Issue 7, September 2007, Pages 1205–1209
نویسندگان
, , , , ,