Influence of load ratio on the biaxial fatigue behaviour and damage evolution in glass/epoxy tubes under tension–torsion loading

An extensive experimental campaign was carried out to understand the influence of the multiaxial stress state and load ratio on the matrix-dominated damage initiation and evolution in composite laminates under fatigue. Tubular glass/epoxy specimens were tested under combined tension–torsion loadings with different values of the load ratio and biaxiality ratio (shear to transverse stress ratio). Results are reported in terms of S–N curves for the first crack initiation and Paris-like diagrams for crack propagation, showing a strong influence of both parameters. Fracture surfaces were also analysed to identify the damage mechanisms at the microscopic scale responsible for the initiation and propagation of transverse cracks. Eventually, a crack initiation criterion presented by the authors in a previous work is applied to the experimental data showing a good agreement.