Galvanic corrosion of titanium coupled to welded titanium in LiBr solutions at different temperatures

The galvanic corrosion generated between the titanium-welded titanium pair has been studied in heavy brine LiBr solutions at 25, 50 and 100 °C under open circuit conditions using a zero-resistance ammeter (ZRA). The results showed that welded titanium was the anode of the pair, so that its corrosion resistance decreases due to the galvanic effect. However, the extremely low galvanic current densities registered by the pair reveal the poor severity of the coupling under the studied conditions. Furthermore, it was observed that the electrodes were in the passive state, increasing the probability of localized corrosion with temperature.