Hot corrosion of YSZ/Al2O3 dispersed NiCrAlY plasma-sprayed coatings in Na2SO4–10 wt.% NaCl melt

This study examines the effect of ytrria stabilized zirconia (YSZ) dispersion on hot corrosion behaviour of NiCrAlY bond coat. Hot corrosion studies were conducted on NiCrAlY and NiCrAlY containing 25, 50 and 75 wt.% YSZ coatings obtained through the air plasma spray technique, in Na2SO4 + 10 wt.% NaCl environment at 800 °C. The results show that YSZ dispersion lowers the overall hot corrosion tendency of the NiCrAlY, though it enhances the inherent hot corrosion tendency of its metallic constituent (NiCrAlY). Furthermore, there exists a threshold oxide level beyond which it adversely affects the hot corrosion of the coating.