Effect of thermal cycles on the corrosion and mechanical properties of UNS S31803 duplex stainless steel

The microstructure and properties of UNS S31803 duplex stainless steel had been investigated following isothermally aging in a temperature range of 450–1000 °C for 10 min, which simulates a fairly long time relative to a weld thermal cycle. The results showed that specimens aged between 600 and 950 °C are subjected to precipitation of secondary phases, such as Cr2N, σ and χ. And the most significant reduction in pitting corrosion resistance and impact energy occurs at 850 °C. Moreover, at aging temperatures below 600 °C, austenite is the preferred site for pitting initiation, which changes to precipitates modified ferrite phase at higher temperatures above 600 °C.