Corrosion behavior of Hastelloy C-276 in supercritical water

The corrosion behavior of a nickel-based alloy Hastelloy C-276 exposed in supercritical water at 500–600 °C/25 MPa was investigated by means of gravimetry, scanning electron microscopy/energy dispersive X-ray spectroscopy, X-ray diffraction and X-ray photoelectron spectroscopy. An oxide scale with dual-layer structure, mainly consisting of an outer NiO layer and an inner Cr2O3/NiCr2O4-mixed layer, developed on C-276 after 1000 h exposure. Higher temperature promoted oxidation, resulting in thicker oxide scale, larger weight gain and stronger tendency of oxide spallation. The oxide growth mechanism in SCW seems to be similar to that in high temperature water vapor, namely solid-state growth mechanism.