The AE method is an effective technique for inspecting corrosion damage of mild steel, such as tank bottom floors. However, the correlation between AE signals and corrosion behaviour for mild steel has not yet been fully clarified. In the present study, the authors considered that the corrosion regions of bottom floors become a strong acid environment by Cl−, as reported in a previous study. Thus, the polarization resistance for the test pieces of mild steel was measured with an AC impedance method under a strong acid environment. It was clear that the polarization resistance indicated the corrosion rate for a test piece of mild steel in the experiments. While measuring the AE signals, the corrosion rate was monitored with a test piece. As a result, the AE signal showed good correlation with the corrosion rates of the test pieces. The corrosion behaviour of the test pieces was then discussed with the corrosion potential measured during the experiments. Furthermore, the cathode current was changed to control the generated hydrogen gas volume. The volume of the hydrogen gas generated from the cathode reaction was correlated to the AE signals.
Journal: Corrosion Science - Volume 51, Issue 8, August 2009, Pages 1679–1684