![عکس صفحه اول مقاله: Stress corrosion cracking and hydrogen embrittlement of sensitized austenitic stainless steels in boiling saturated magnesium chloride solutions Stress corrosion cracking and hydrogen embrittlement of sensitized austenitic stainless steels in boiling saturated magnesium chloride solutions](/preview/png/1471586.png)
Stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of the sensitized stainless steels of type 304, 310 and 316 were investigated as a function of test temperature in boiling saturated magnesium chloride (MgCl2) solutions under a constant applied stress condition. The test temperature dependence of fracture appearance and three parameters of time to failure (tf), steady-state elongation rate (lss) and transition time to time to failure ratio (tss/tf) suggests that type 304 suffered SCC and HE, while type 316 suffered only HE and type 310 SCC. It was also found that the test temperature dependence of three parameters for the sensitized type 304 and 310 was almost similar to that of the solution annealed stainless steels, whereas that of type 316 showed a clear difference between sensitized and solution annealed specimens. The relationships between the logarithms of the time to failure and the steady-state elongation rate became a straight line for all stainless steels. However, its slope depended upon the fracture mode; −2.0 for SCC and −1.5 for HE. This showed that the steady-state elongation rate was the parameter for predicting the time to failure for the stainless steels in the MgCl2 solutions. The results obtained were explained in terms of martensite transformation, hydrogen entry site, sensitization, and so on.
Journal: Corrosion Science - Volume 50, Issue 8, August 2008, Pages 2353–2359