The present paper focuses on the study of SCC behaviour of a new Al–Cu–Li alloy. For this purpose, two conventional media – NaCl and NaCl + H2O2 – were used for comparison with commercial alloys 7075 and 8090. This new alloy shows lower susceptibility to SCC than conventional alloys as it does not undergo environmentally-induced embrittlement in NaCl solutions and in 1 M NaCl + 0.3% H2O2 in which the 7075 and 8090 alloys, respectively, undergo environmentally-induced fracture.Solution composition was modified in order to determine the environmental conditions and strain rates under which this new alloy will crack due to a stress corrosion cracking phenomenon. The addition of 0.6 M sulphates to 1 M NaCl + 0.3% H2O2 solution allows the definition of a range of strain rate (between 10−7 and 10−6 s−1) in which this new alloy undergoes stress corrosion cracking.
Journal: Corrosion Science - Volume 48, Issue 12, December 2006, Pages 4113–4126