SiC(SCS-6) fiber-reinforced Ti3AlC2 matrix composites: Interfacial characterization and mechanical behavior
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
SiC(SCS-6) fiber-reinforced Ti3AlC2 matrix composites: Interfacial characterization and mechanical behavior
چکیده انگلیسی

In this study, the carbon-rich coated silicon carbide (SiC) fiber-reinforced Ti3AlC2 matrix composites having two distinct fiber concentrations had been prepared by hot-pressing at 1250 °C and 1300 °C, respectively. Interfacial reaction layer between the fiber and the matrix was characterized by using field emission scanning electron microscopy (FE-SEM). Elemental distribution maps of the interfacial reaction layer were quantitatively examined by energy-dispersive spectroscopy (EDS). The effects of processing temperature on the interfacial reaction layer formed during hot-pressing were assessed. In addition, the flexural strength and fracture behavior of the resulting composites depended on the processing temperatures as well as on the fiber volume fraction. Noncatastrophic fracture behavior was observed only for 15 vol% SiC fiber-containing composite processed at 1250 °C.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 35, Issue 5, May 2015, Pages 1375–1384
نویسندگان
, , , , ,