Interactions between a poly(vinyl)silazane and Al2O3 or Y2O3-stabilised ZrO2 fillers were studied during the fabrication of polysilazane-derived bulk ceramics in order to investigate the influence of oxide fillers on resulting properties. Specimens were produced by coating of the filler powders with the polysilazane, warm-pressing of the resulting composite powders, and pyrolytic conversion in flowing N2 at various temperatures between 1000 °C and 1400 °C. Significant differences in densification were observed, depending on the filler used. Reactions between the polysilazane-derived matrix and Al2O3 or ZrO2 at temperatures ≥1300 °C resulted in the formation of Si5AlON7 or ZrSiO4, respectively. Reactivity in the polysilazane-derived component was a result of SiO2 contamination caused primarily by adsorbed species on the filler particle surface. Knowledge of polysilazane/filler interface processes is found to be decisive for the prediction of properties such as shrinkage and porosity, which heavily influence performance of a material.
Journal: Journal of the European Ceramic Society - Volume 31, Issue 15, December 2011, Pages 3021–3031