Fabrication and optical characterizations of Yb, Er codoped CaF2 transparent ceramic
چکیده انگلیسی

Nanoparticles of Yb, Er codoped calcium fluoride were obtained by a co-precipitation method. Scanning electron microscope (SEM) and X-ray powder diffraction (XRD) analysis showed that the obtained nanoparticles were single fluorite phase with grains size around 30–50 nm. Yb, Er:CaF2 transparent ceramics were fabricated by hot pressing (HP) the nanoparticles at a temperature of 800 °C in a vacuum environment. For a 2 mm thickness ceramic sample, the transmittance at 1200 nm reached about 83%. Microstructures were characterized using SEM analysis, and the average grain size was about 700 nm. Grain boundaries of the ceramic sample were clean and no impurities were detected. The absorption, upconversion and infrared emission spectra of transparent ceramic sample under 978 nm excitation were measured and discussed.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 34, Issue 16, December 2014, Pages 4389–4394
نویسندگان
, , , ,