Environment-friendly deposition of SiCN interlayer for reinforcing carbon fibers in C/SiC composites

Several C/SiC composites with no interlayer, single pyrocarbon (PyC) interlayer and PyC/SiCN interlayer were fabricated by polymer infiltration and pyrolysis process. The microstructure and mechanical properties were investigated. The results verified that SiCN interlayer was formed on carbon fibers. Both bulk density and flexural stress of C/SiC composite with PyC/SiCN interlayer were slightly higher than composite fabricated with single PyC interlayer. When the weight fraction of SiCN interlayer in the composite was about 18 wt%, the flexural stress of the composite was enhanced to 416 MPa from 352 MPa for composite with single PyC interlayer. The observations of pulled-out fibers on fracture surfaces revealed non-catastrophic fracture features for PyC/SiCN deposited C/SiC composite.