The residual stresses in YAG phase in directionally solidified eutectic (DSE) Al2O3/Y3Al5O12 (YAG) ceramic composite were estimated by X-ray diffraction technique. The YAG skeleton specimen without Al2O3 phase, extracted from the composite, was used as a thermally-induced stress-free reference specimen. The X-ray stress measurements with Cu Kα irradiation were performed on the two planes: parallel and perpendicular to the solidification direction. The estimated residual stresses on average were −220 MPa and −157 MPa on the planes parallel and perpendicular to the solidification direction, respectively. The measured residual stresses were described fairly well by the calculation based on a lamellar model under the condition of the stress-free temperature 1400–1600 K.
Journal: Journal of the European Ceramic Society - Volume 28, Issue 12, August 2008, Pages 2319–2324