Formation and crystallization of zinc borosilicate glasses: Influence of the ZnO/B2O3 ratio

• Borosilicate glasses with ZnO between 60 and 65% were successfully prepared.
• Heat-treatment of the glasses induced the precipitation of willemite (Zn2SiO4).
• Willemite formation was favored by an increasing ZnO/B2O3 ratio.
• Transparent and translucent willemite glass-ceramics were obtained.

Different glasses based on the ZnO–B2O3–SiO2 system, with a ZnO content ≥ 60 mol% and a fixed SiO2 content (20 mol%), were synthesised using a melt-quenching method. Glass samples with zinc oxide concentrations as high as 65 mol% were prepared successfully without deteriorating the glass-forming ability. The glass samples were submitted to controlled heat-treatments, and the effect of the ZnO/B2O3 molar ratio on the formation of crystalline phases within the glass matrix was investigated by means of differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM).DTA results indicated that the glass transition and the onset crystallization temperatures of the studied glasses tended to increase with the increment on the ZnO/B2O3 ratio. XRD data showed that the zinc binary crystalline phases, willemite (Zn2SiO4), a zinc orthosilicate, and zinc borate (Zn3B2O6) could be present in the crystallized glasses, depending on the heat-treatment conditions. The formation of willemite was promoted by an increasing ZnO/B2O3 ratio. Microstructural observations performed by SEM indicated that under controlled experimental parameters (glass composition, heat-treatment temperature and time) the precipitation of nanocrystals within the glass matrix can be achieved, resulting in transparent and translucent willemite glass-ceramics.