Orientation-dependent energy-storage performance and electrocaloric effect in PLZST antiferroelectric thick films
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
Orientation-dependent energy-storage performance and electrocaloric effect in PLZST antiferroelectric thick films
چکیده انگلیسی


• 1.5-μm-(Pb0.97La0.02)(Zr0.73Sn0.22Ti0.05)O3 AFE thick films with (111), (110), and (100) orientations were prepared via a sol-gel method.
• Enhanced energy-storage performance and ECE were enhanced by orientation control.
• Enhanced energy-storage density of 13.5 J/cm3 and electrocaloric effect of ΔT = 28.1 °C were obtained in PLZST(111) thick film.

The enhancement of the energy-storage performance and electrocaloric effect (ECE) was achieved via orientation control. The 1.5-μm-(Pb0.97La0.02)(Zr0.73Sn0.22Ti0.05)O3 (PLZST) antiferroelectric (AFE) thick films with (111), (110), and (100) crystallographic orientations were successfully prepared via a sol-gel method. It was found that both the enhanced energy-storage density of 13.5 J/cm3 at 900 kV/cm and the corresponding temperature reduction of ΔT = 28.1 °C at room temperature were obtained in the PLZST thick film with (111) orientation due to a high polarization. Moreover, these films with different orientations display a small leakage current density at the room temperature. These results suggest that both energy-storage properties and cooling performance in AFEs could be optimized by the proper orientation control.

Figure optionsDownload as PowerPoint slide