• Nanocrystalline Fe–Al–Cu catalysts with high surface area were synthesized.
• Cr-free iron based catalysts were evaluated in HTS reaction.
• Taguchi method of experimental design was used to optimize the preparation parameters.
• The sample prepared under optimized conditions showed the highest activity.
• The sample prepared under optimized conditions showed the highest surface area.
Nanocrystalline Cr-free Fe–Al–Cu catalysts with high surface area and mesoporous structure was prepared by coprecipitation method and employed in high temperature water gas shift reaction. Several parameters such as pH, aging temperature and aging time were optimized by the Taguchi method of experimental design. The sample prepared under optimized conditions showed a high surface area of 208 m2 g−1, pore size of 3.76 nm and theoretical particle size of 5.47 nm after calcination at 400 °C for 4 h. This catalyst illustrated the highest CO conversion compared to other prepared catalysts. These results confirmed that the Taguchi method is an effective method of determining the optimum parameters in preparation process of high temperature water gas shift catalyst. Moreover, the effect of calcination temperature, GHSV and steam/gas ratio on the catalytic performance of optimized Fe–Al–Cu catalyst was investigated.
Figure optionsDownload as PowerPoint slide
Journal: Materials Research Bulletin - Volume 70, October 2015, Pages 229–235