Lattice thermal expansion of the solid solutions (La1 − xSmx)2Ce2O7

• Sm-doped La2Ce2O7 was prepared by the coprecipitation–calcination method.
• In situ HT-XRD measurements revealed that is much stable than 8YSZ.
• Its thermal expansion is better than 8YSZ.

A series of solid solutions with the general formula (La1 − xSmx)2Ce2O7 (0.0 ≤ x ≤ 1.0) were prepared by the coprecipitation–calcination method. The products obtained were characterized by powder X-ray diffraction for phase purity. It was observed that La3+ and Sm3+ can form complete solid solution in (La,Sm)2Ce2O7 with defect-fluorite-type phase. The unit cell parameters of these solutions were calculated by a least squares method and the lattice parameters decreased linearly as x increased. The lattice thermal expansion behavior of (La1 − xSmx)2Ce2O7 (0.0 ≤ x ≤ 1.0) was investigated by high-temperature X-ray diffraction in the temperature range 298–1623 K. The lattice parameters aT of all the solutions at different temperature can be expressed as aT = a + bT + cT2. As x < 1, the thermal expansion has a sudden decrease at ca. 473 K. The coefficients of lattice thermal expansion of Sm2Ce2O7 were 10.2–13.6 × 10−6 K−1 from 298 to 1623 K, and without the thermal contraction at low temperature. The materials show positive or negative thermal expansion due to the asymmetric anharmonic vibration.

Figure optionsDownload as PowerPoint slide