Characterization of silver/polystyrene nanocomposites prepared by in situ bulk radical polymerization
ترجمه فارسی عنوان
خصوصیات نانوکامپوزیت های نقره / پلی استایرن به واسطه پلیمریزاسیون رادیکالی بسپار در محل تزریق
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
چکیده انگلیسی


• Synthesis and characterization of polystyrene nanocomposites based on Ag nanoparticles.
• The glass transition temperature decreased in nanocomposites with respect to the pure polymer.
• Resistance of the polymer to thermal degradation enhanced with Ag nanoparticles content.

Nanocomposites (NCs) with different content of silver nanoparticles (Ag NPs) embeded in polystyrene (PS) matrix were prepared by in situ bulk radical polymerization. The nearly monodisperse Ag NPs protected with oleylamine were synthesized via organic solvo-thermal method and further used as a filler. The as-prepared spherical Ag NPs with diameter of 7.0 ± 1.5 nm were well dispersed in the PS matrix. The structural properties of the resulting Ag/PS NCs were characterized by transmission electron microscope (TEM) and Fourier transform infrared (FTIR) spectroscopy, while optical properties were characterized using optical absorption measurements. The gel permeation chromatography (GPC) measurements showed that the presence of Ag NPs stabilized with oleylamine has no influence on the molecular weight and polydispersity of the PS matrix. The influence of silver content on the thermal properties of Ag/PS NCs was investigated by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The results indicated that resistance of PS to thermal degradation was improved upon incorporation of Ag NPs. The Ag/PS NCs have lower glass transition temperatures than neat PS because loosely packed oleylamine molecules at the interface caused the increase of free volume and chain segments mobility near the surface of Ag NPs.

Figure optionsDownload as PowerPoint slide