• Template-free synthesis of rods of CoMoO4 was achieved under hydrothermal conditions.
• The width of the rods is about 100 nm and the length varies from 1 to 5 μm.
• Low temperature and pressure of synthesis favour the formation of longer rods.
The effect of pressure and temperature on the synthesis of cobalt-molybdenum oxides and their characterisation is herein reported. The synthesis was performed under hydrothermal conditions without any template. It was found that the experimental conditions affect the physical properties of the CoMoO4. SEM images demonstrate that the synthesised powder is comprised of rods, and the width of the structures is about 100 nm but the length varies from about 5 μm to less than 1 μm. Low temperature and pressure favour the formation of longer rods.
Figure optionsDownload as PowerPoint slide
Journal: Materials Research Bulletin - Volume 48, Issue 11, November 2013, Pages 4614–4617