Exchange-spring mechanism of soft and hard ferrite nanocomposites

• Exchange-spring behaviour of soft and hard ferrites was studied.
• XRD patterns indicated soft and hard ferrites as fcc and hcp structure.
• Hysteresis loops indicate wide difference in coercivity of soft and hard phases.
• Nanocomposites produced convex hysteresis loop characteristic of single-phase.

The paper reports exchange-spring soft and hard ferrite nanocomposites synthesized by chemical co-precipitation with or without the application of ultrasonic vibration. The composites contained BaFe12O19 as the hard phase and CoFe2O4/MgFe2O4 as the soft phase. X-ray diffraction patterns of the samples in the optimum calcined condition indicated the presence of soft ferrites as face-centred cubic (fcc) and hard ferrites as hexagonal close packed (hcp) structure respectively. Temperature dependence of magnetization in the range of 20–700 °C demonstrated distinct presence of soft and hard ferrites as magnetic phases which are characterized by wide difference in magnetic anisotropy and coercivity. Exchange-spring mechanism led these nanocomposite systems to exchange-coupled, which ultimately produced convex hysteresis loops characteristic of a single-phase permanent magnet. Fairly high value of coercivity and maximum energy product were observed for the samples in the optimum calcined conditions with a maximum applied field of 1600 kA/m (2 T).

Figure optionsDownload as PowerPoint slide