![عکس صفحه اول مقاله: Hydrothermal-induced growth of Ca10V6O25 crystals with various morphologies in a strong basic medium at different temperatures Hydrothermal-induced growth of Ca10V6O25 crystals with various morphologies in a strong basic medium at different temperatures](/preview/png/1489049.png)
The Ca10V6O25 crystals with various morphologies were synthesized by a facile hydrothermal method in a strong basic medium. The effects of the pH of synthesizing solution, hydrothermal reaction temperature and time on the morphology and crystallinity of Ca10V6O25 powders were investigated. The as-synthesized powders were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, UV–vis spectrophotometer and vibrating sample magnetometer. The experimental results demonstrate that phase-pure Ca10V6O25 powders could be hydrothermally obtained at temperatures ranging from 120 °C to 180 °C for 12–48 h with the pH ≥ 12.5 of synthesizing solution. The morphology of Ca10V6O25 powders was strongly dependent on the synthesis parameters, such as pH, temperature and time. The Ca10V6O25 microspheres were obtained at 180 °C for 48 h with the pH = 12.5 of synthesizing solution. The UV–vis diffuse reflectance spectra have shown that the Ca10V6O25 powders efficiently absorb UV light with an absorption edge at about 380 nm. All the samples noticeably exhibit a superparamagnetic behavior with a nearly zero magnetic remanence (remanent magnetization). The hydrothermally synthesized Ca10V6O25 powders may be employed as a potential candidate in novel electronic and biomedical applications.
Figure optionsDownload as PowerPoint slideHighlights
► C10V6O25 crystals are hydrothermally grown in a strong basic medium.
► With the increase in the pH the average crystallite size of Ca10V6O25 increases.
► Morphological transformation occurs with increasing reaction temperature.
► Ca10V6O25 powders absorb UV light with the absorption edge at ∼380 nm.
► Ca10V6O25 powders demonstrate a superparamagnetic behavior.
Journal: Materials Research Bulletin - Volume 48, Issue 4, April 2013, Pages 1388–1396