ZnO films and nanorod/shell arrays electrodeposited on PET-ITO electrodes

In this work, ZnO films, nanorod and nanorod/shell arrays were synthesized on the surface of PET-ITO electrodes by electrochemical methods. ZnO films with high optical transmittance were prepared from a zinc nitrate solution using a pulsed current technique with a reduced pulse time (3 s). The X-ray diffraction pattern of ZnO film deposited on PET-ITO electrode showed that it has a polycrystalline structure with preferred orientations in the directions [0 0 2] and [1 0 3]. ZnO nanorods were synthesized on electrochemical seeded substrate in an aqueous solution containing zinc nitrate and hexamethylenetetramine. In order to increase the stability of PET-ITO electrode to electrochemical and chemical stresses during ZnO nanorods deposition the surface of the electrode was treated with a 17 wt% NH4F aqueous solution. Electrochemical stability of PET-ITO electrode was evaluated in a solution containing nitrate ions and hexamethylenetetramine. ZnO nanorod/shell arrays were fabricated using eosin Y as nanostructuring agent. Photoluminescence spectra of ZnO nanorod and ZnO nanorod/shell arrays prepared on the surface of PET-ITO electrode were discussed comparatively. By employing the 1.5 μm-length ZnO nanorod/shell array covered with a Cu2O film a photovoltaic device was fabricated on the PET-ITO substrate.

Figure optionsDownload as PowerPoint slideHighlights
► A pulsed electrodeposition technique was used for producing ZnO films on PET-ITO.
► A ZnO nanorod/shell array was prepared on PET-ITO electrode.
► A ZnO nanorod/shell-Cu2O film solar cell was achieved on the PET-ITO support.