Gel-like properties of MCM-41 material and its transformation to MCM-50 in a caustic alkaline surround

MCM-41 material, prepared by sol–gel method, reveals gel-like properties in a caustic alkaline environment, i.e., 6 M potassium hydroxide (KOH) electrolyte. The gellation of MCM-41 starts at a KOH weight ratio of 40 wt.%. The structural change of the material is verified with X-Ray diffractograms and supported by observation using Scanning Electron Microscope (SEM). As the KOH weight ratio increases, the MCM-41 hexagonal arrays structure gradually transforms into MCM-50 lamellar structure before disappearing completely at 80 wt.% KOH. The MCM gel phase is further characterized by rotational viscometry and texture analysis. The gel phase shows shear thinning or pseudoplastic behavior and possesses homogeneous matrix structure.

Figure optionsDownload as PowerPoint slideHighlights
► MCM-41 material transforms gradually into MCM-50 lamellar gel upon controlled exposure to 6 M KOH.
► The formation of MCM-50 ordered gel structure occurs at KOH weight content of 40–70 wt. %.
► MCM gel phase shows pseudoplastic behavior and possesses homogeneous matrix texture.