The synergistic effect of cationic surfactant (CTAB) and anionic surfactant (SDS) for the modification of Ca-montmorillonite (Ca-MMT) has been developed, and the novel cation–anion modified organomontmorillonite (MMT–CTAB–SDS) was prepared. X-ray diffraction (XRD) analysis indicates that the interlayer spacing of montmorillonite was well expanded by the intercalation of CTAB and SDS and the basal spacing increased from 1.54 nm (Ca-MMT) to 5.30 nm (MMT–CTAB–SDS). Thermogravimetric analysis (TG) showed that the MMT–CTAB–SDS displayed excellent heat resistance. Scanning electron microscopy (SEM) analysis proved that the MMT–CTAB–SDS exhibited excellent dispersion property and the plates with few silicate layers can be observed. Contact angle tests indicated that the hydrophilicity of MMT–CTAB–SDS was lower than that of Ca-MMT and higher than that of MMT–CTAB. It was verified that SDS contributed to expanding the interlayer space, further improved the heat resistance of the MMT–CTAB and decreased the surface energy of the MMT–CTAB–SDS particles.
Figure optionsDownload as PowerPoint slideHighlights
► The basal spacing of MMT–CTAB–SDS reaches 5.30 nm.
► MMT–CTAB–SDS shows perfect dispersion property and excellent heat resistance.
► SDS helped to improve the heat resistance and decrease the surface energy of the MMT–CTAB–SDS particles.