![عکس صفحه اول مقاله: Studies on optical, chemical, and electrical properties of rapid SiO2 atomic layer deposition using tris(tert-butoxy)silanol and trimethyl-aluminum Studies on optical, chemical, and electrical properties of rapid SiO2 atomic layer deposition using tris(tert-butoxy)silanol and trimethyl-aluminum](/preview/png/1489703.png)
Rapid SiO2 atomic layer deposition (ALD) was used to deposit amorphous, transparent, and conformal SiO2 films using tris(tert-butoxy)silanol (TBS) and trimethyl-aluminum (TMA) as silicon oxide source and catalytic agent, respectively. The growth rate of the SiO2 films drastically increased to a maximum value (2.3 nm/cycle) at 200 °C and slightly decreased to 1.6 nm/cycle at 275 °C. The SiO2 thin films have C–H species and hydrogen content (∼8 at%) at 150 °C because the cross-linking rates of SiO2 polymerization may reduce below 200 °C. There were no significant changes in the ratio of O/Si (∼2.1) according to the growth temperatures. On the other hand, the film density slightly increased from 2.0 to 2.2 although the growth rate slightly decreased after 200 °C. The breakdown strength of SiO2 also increases from 6.20 ± 0.82 to 7.42 ± 0.81 MV/cm. These values suggest that high cross-linking rate and film density may enhance the electrical property of rapid SiO2 ALD films at higher growth temperature.
Journal: Materials Research Bulletin - Volume 47, Issue 10, October 2012, Pages 3004–3007