Fast synthesis, formation mechanism, and control of shell thickness of CuS–polystyrene core–shell microspheres

The silanol-modified polystyrene microspheres were prepared through dispersion polymerization. Then copper sulfide particles were grown on silanol-modified polystyrene through sonochemical deposition in an aqueous bath containing copper acetate and sulfide, released through the hydrolysis of thioacetamide. The resulting particles were continuous and uniform as characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Fourier transform infrared, thermogravimetric analysis and UV–vis absorption spectroscopy were used to characterize the structure and properties of core–shell particles. The results showed the coating thickness of CuS shell can be controlled by the amount of silanol and the UV–vis absorption intensity of PSt/CuS composite also changed with the coating thickness of CuS.

Core–shell structure PSt/CuS were prepared using polystyrene which were modified by 3-methacryloxypropyltrimethoxysilane as template. The coating thickness of CuS can be controlled by the amount of 3-methacryloxypropyltrimethoxysilane and the UV–vis absorption intensity of PSt/CuS composite also changed with the coating thickness of CuS.Figure optionsDownload as PowerPoint slideHighlights
► Core–shell structure PSt/CuS were prepared using silanol-modified polystyrene microspheres as template.
► The coating thickness of core–shell structure PSt/CuS can be controlled by a simple method.
► The UV–vis absorption intensity of PSt/CuS composite also changed with the coating thickness of CuS.