Preparation and properties of negative thermal expansion Zr2WP2O12 ceramics

Using solid-state reaction method, Zr2WP2O12 powder was synthesized for this study. The optimum heating condition was 1200 °C for 4 h. The obtained powder was compacted and sintered. The relative density of the Zr2WP2O12 ceramics with no sintering additive was 60%. That of samples sintered with more than 0.5 mass% MgO was about 97%. The average grain size (D50), as estimated from the polished surface of a sample sintered at 1200 °C for 4 h was about 1 μm. The obtained ceramics showed a negative thermal expansion coefficient of about −3.4 × 10−6 °C−1. Young's modulus, Poisson's ratio, three-point bending strength, Vickers microhardness, and fracture toughness of the obtained ceramics were, respectively, 74 GPa, 0.25, 113 ± 13 MPa, 4.4 GPa and 2.3 MPa m1/2.