• Ce-doped LiF–SrF2 eutectic scintillators are reported for the first time.
• The optimum layer thickness was determined experimentally.
• The brightest sample exhibited the light yield of 5500 ph/n.
• In scintillation decay times, both Ce3+ 5d–4f and STE emissions were observed.
Ce 0.1% doped LiF–SrF2 eutectic scintillators were produced by vertical Bridgman method at various solidification rates of 1, 5, 20, 80, 320, and 1280 mm/hr. The LiF contained 95% of 6Li. The SEM images of the samples solidified at 1–80 mm/hr demonstrated clear lamellar structures. The α-ray induced radioluminescence spectra of the scintillators had intense emission peak at 310 and 330 nm due to the emission from Ce3+ 5d–4f transition of Ce:SrF2 layers. When the samples were irradiated with 252Cf neutrons, they exhibited almost the same light yields of 4500–5500 ph/n and typical decay times of 120–160 ns. The optimal layer thickness of LiF–SrF2 was determined to be 0.9 μm.
Journal: Optical Materials - Volume 35, Issue 7, May 2013, Pages 1449–1454