Scratch-induced deformation in fine- and ultrafine-grained bulk alumina

The nanoscratch behavior of two bulk α-alumina samples with 1.3 μm and 290 nm average grain sizes, respectively, was investigated using a nanoindenter in scratch mode, in combination with atomic force and scanning electron microscopy. A ductile to brittle transition was observed in the fine-grained sample, while the ultrafine-grained sample exhibited predominantly ductile deformation with a fish-bone feature indicative of a stick–slip mechanism. These findings suggest that grain refinement can increase the potential for plastic deformation in ceramics.