Bainitic transformation behavior studied by simultaneous neutron diffraction and dilatometric measurement

Bainitic transformation behavior has firstly been observed using in situ neutron diffraction with an angular dispersive method for a hard bainite steel. The dilatometric measurement was carried out simultaneously with the neutron experiment where changes in (1 1 1) austenite and (1 1 0) ferrite diffraction profiles were monitored during heating, cooling and holding at a transformation temperature. The neutron experiments results agree with dilatometry results. They appear to have found that the austenite peak broadening occurs after the onset of bainitic transformation but not before.