Recrystallization textures of the M{1 1 3}〈1 1 0〉 and P{0 1 1}〈4 5 5〉 orientations in a supersaturated Al–Mn alloy

The evolution of recrystallization texture in a supersaturated Al–Mn alloy was investigated by X-ray diffraction. A new recrystallization texture {1 1 3}〈1 1 0〉 was found in this alloy in addition to the P recrystallization texture. The formation of the M and P recrystallization textures depended strongly on annealing temperature. Low-temperature annealing of the cold-rolled sheets resulted in strong M and P recrystallization textures. The strength of the M and P recrystallization textures decreased with increasing annealing temperature.