Synthesis and electrical properties of (LiCo3/5Fe1/5Mn1/5)VO4 ceramics

(LiCo3/5Fe1/5Mn1/5)VO4 ceramic was synthesized via solution-based chemical method. X-ray diffraction analysis was carried out on the synthesized powder sample at room temperature, which confirms the orthorhombic structure with the lattice parameters of a = 10.3646 (20) Å, b = 3.7926 (20) Å, c = 9.2131 (20) Å. Field emission scanning electron microscopic analysis was carried out on the sintered pellet sample that indicates grains of unequal sizes (∼0.1 to 2 μm) presents average grains size with polydisperse distribution on the surface of the ceramic. Complex impedance spectroscopy (CIS) technique is used for the study of electrical properties. CIS analysis identifies: (i) grain interior, grain boundary and electrode–material interface contributions to electrical response (ii) the presence of temperature dependent electrical relaxation phenomena in the ceramics. Detailed conductivity study indicates that electrical conduction in the material is a thermally activated process. The variation of A.C. conductivity with frequency at different temperatures obeys Jonscher's universal law.

Figure optionsDownload as PowerPoint slide