Phase decomposition study in CoxFe3−xO4 iron cobaltites: Synthesis and structural characterization of the spinodal transformation
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
Phase decomposition study in CoxFe3−xO4 iron cobaltites: Synthesis and structural characterization of the spinodal transformation
چکیده انگلیسی

CoxFe3−xO4 iron cobaltites (1.21 < x < 2.35) have been prepared in the form of submicronic particles from mixed oxalic precursors heat treated at 900 and 600 °C. The samples obtained at 900 °C are made of a single spinel phase in which Co2+ and Fe3+ ions are distributed in both octahedral and tetrahedral sites and Co3+ ions are only located in the octahedral sublattice. For heat treatments carried out at 600 °C two spinel phases are formed according to the phase diagrams. Pure Co1.7Fe1.3O4 oxide annealed at 700 °C progressively transformed into two iron-rich and cobalt-rich spinel phases, respectively. More than 120 h of heat treatment is required to get the complete decomposition of the pristine oxide. At the beginning this oxide is submitted to a spinodal transformation. Alternating regions of iron-rich and cobalt-rich spinels are then created. The periodicity of the nanostructuration of the material is estimated to be close to 5 nm.

Figure optionsDownload as PowerPoint slide

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Solid State Sciences - Volume 10, Issue 5, May 2008, Pages 550–556
نویسندگان
, , , ,