Determinations of enthalpy and partial molar enthalpy in the alloys Bi–Cd–Ga–In–Zn, Bi–Cd–Ga–Zn and Au–Cu–Sn

• Thermodynamic properties of alloys in the study in given conditions were treated.
• The activity of Bi seen in all models shows greatly positive deviation from ideality.
• The enthalpy of Sn shows small negative values in xAu/xCu = 1 at 900 K.
• The activity of Sn shows negative deviation from ideality in the same conditions.

In the present study, the relations of thermodynamic associated with Chou's general solution model (GSM), the models of Muggianu and Toop have been used in order to calculate the mixing enthalpy and partial molar mixing enthalpy of mixing of Bi–Cd–Ga–In–Zn, Bi–Cd–Ga–Zn with equimolar section at a temperature of 730 K and Au–Cu–Sn with the section xAu/xCu = 1/1 on the entire molar fraction range as a function of alloy composition at a temperature of 900 K. Some negativities are reported in the selected alloys mentioned above, particularly at high temperatures for the human health as well as difficulties in experimental measurement and high costs. Moreover, aim of us is to close the current article gap seen in the literature. In order to close the current gap seen in the literature, the article on the thermodynamic properties of the Bi–Cd–Ga–In–Zn alloys are presented in this study.