Synthesis of Ni/graphene sheets by an electroless Ni-plating method
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
شیمی مواد
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Ni/graphene sheets were synthesized from graphene oxide sheets using electroless Ni-plating in a NiSO4 solution, with NaBH4 as a reducing agent. The samples were characterized by X-ray diffraction, scanning and transmission electron microscopy. Ni deposited on the surface of the reduced graphene oxide sheets had a high dispersion without aggregation, although the amount of Ni was as high as 32.9% by mass. The stacking of Ni/graphene sheets resulted in the formation of meso- and macropores. Nitrogen adsorption showed that the meso- and macropores had a slit shape and that the Brunauer-Emmett-Teller specific surface area reached 91 m2/g. The average pore size calculated by the Barret-Joyner-Halenda method from desorption studies was 3.83 nm, with a pore volume of 0.28 cm3/g.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: New Carbon Materials - Volume 27, Issue 1, February 2012, Pages 35-41
Journal: New Carbon Materials - Volume 27, Issue 1, February 2012, Pages 35-41
نویسندگان
Qing-hua HU, Xi-tang WANG, Hao CHEN, Zhou-fu WANG,