Aging effects on the microstructures and mechanical properties of the Ti–20Zr–6.5Al–4V alloy
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
Aging effects on the microstructures and mechanical properties of the Ti–20Zr–6.5Al–4V alloy
چکیده انگلیسی

This study aims to evaluate the effects of heat treatment on the structural evolution and mechanical properties of the Ti–20Zr–6.5Al–4V (wt%) alloy. The alloy was melted via electromagnetic induction, homogenized, transus-processed, solid-solubilized, and then aged at different temperatures (from 450 °C to 700 °C) for 120 min. X-ray diffraction was used to characterize the phase compositions in the alloy under different conditions. During the solution treatment process, the alloy underwent the following phase transformation: β→α+β (retained)+α″+fcc phase. Martensite α″ and β phases transformed into the α phase after the aging treatment. The fcc phase became completely dissolved when the aging temperature increased to 700 °C. At this temperature, the mechanical properties of the alloy reached their optimum combination at σb=1437 MPa, σ0.2=1294 MPa, and ε=6.69%.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 559, 1 January 2013, Pages 474–479