Radial and longitudinal variations in the Young's modulus of a Zr55Al10Ni5Cu30 metallic glass cylindrical rod were examined by means of nanoindentation. The metallic glass rod, 2.4 mm in diameter, was prepared using a novel mold-casting method designed to suppress crystallization resulting from the heterogeneous nucleation originating from slag covering a molten alloy. In this study, Young's modulus was measured using a multiple partial unloading technique with a spherical indenter. In general, it is assumed that the cooling rate of a metallic glass rod depends on the radius of its cross section. However, no significant difference was found in the measured Young's modulus.
► We cast a bulk metallic glass rod by using a novel horizontal mold.
► This mold can quench a molten alloy slowly.
► The metallic glass rod is structurally relaxed and becomes uniform.
► The variation in the Young's modulus of the rod is negligible.
Journal: Materials Science and Engineering: A - Volume 534, 1 February 2012, Pages 459–464