The effects of Co and Ti additions on the microstructures and compressive strength of the Ni-based superalloy Udiemt710 (U710) were investigated. The preliminary results showed that the Ni3Ti-type (η) phase was observed in the alloys with low Co and Ti content; while a (NixCo1−x)3Ti phase with a hexagonal structure was detected in the alloys with high Co and Ti content. The γ′ → η → (NixCo1−x)3Ti phase transformation was discussed in terms of Co and Ti contents. The γ′ morphology changed from spherical to cuboidal with increasing Co and Ti content. Compressive tests showed that the alloys with Co and Ti addition possessed higher yield strength than the base alloy, U710. The strength increase could be ascribed to solid–solution strengthening of the γ and γ′ phases as a result of the Co and Ti additions, and the higher volume fraction of γ′ in the new alloys.
► The effects of Co and Ti addition on the microstructures and compressive strength of the Ni-based superalloy Udiemt710 were investigated.
► The γ′ morphology changed from spherical to cuboidal with Co and Ti addition.
► η Phase and (NixCo1−x)3Ti phase were found in the new alloys.
► The γ′ → η → (NixCo1−x)3Ti phase transformation is discussed in terms of Co and Ti content.
► The alloys with Co and Ti addition possessed higher yield strength than the base alloy, U710.
Journal: Materials Science and Engineering: A - Volume 528, Issue 27, 15 October 2011, Pages 7851–7856