کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
1580758 | 1514848 | 2009 | 7 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
Creep-damage assessment of high chromium heat resistant steels and weldments
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The microstructural changes during the creep damage process were investigated on 10Cr-1Mo-1W-VNbN steel forging and the weldment of Mod.9Cr steel-12Cr steel casting, using a scanning electron microscope equipped to take electron backscatter diffraction (EBSD) patterns, and by nano-indentation. Creep rupture and interrupted creep test samples were cut at mid-section along longitudinal direction and inverse pole figures (IPF) and Kernel average misorientation (KAM) maps were obtained from EBSD patterns. Grain size and block size were clearly identified by IPF maps and proved to be good measures of creep time fraction. Area-averaged KAM (KAMave) was shown to be effective for evaluating dislocation microstructural changes during creep and for creep damage evaluation of the forging material. Nano-indentation tests were conducted at the same position in EBSD measurement, which showed a good correlation between hardness value and the square root of KAMave. The creep damage estimation curves of KAMave were obtained as a function of creep time fraction. For the fine-grained, heat-affected zone, area fraction of creep voids and grain size measured by EBSD were good measures of creep damage, while KAMave was not such a good measure.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volumes 510â511, 15 June 2009, Pages 195-201
Journal: Materials Science and Engineering: A - Volumes 510â511, 15 June 2009, Pages 195-201
نویسندگان
Kazunari Fujiyama, Keita Mori, Takahide Matsunaga, Hirohisa Kimachi, Takashi Saito, Takehisa Hino, Ryuichi Ishii,